A new OSL phosphor CaSO₄:Eu was developed. The phosphor shows good OSL sensitivity which is about 55% of commercially available Al₂O₃:C. The phosphor also shows good TL sensitivity and the dosimetric peak, which appears around 186°C, has sensitivity nearly 50% of Al₂O₃:C. After OSL readout of the irradiated sample, the TL peak around 250°C depletes completely, with partial depletion of peak around 186°C. Since the traps responsible for the high temperature peak are involved for the observed OSL, the sample shows low post-irradiation fading. The OSL decay is similar to Al₂O₃:C. Thus this phosphor due to its good OSL sensitivity, linear dose response, low fading and simple preparation technique could be useful for radiation dosimetry applications.