In the present work, we have studied the hydrogen absorptionedesorption properties of the Ti₂CrV alloy, and effect of cycling on the hydrogen storage capacity. The material has been characterized for the structure, morphology, pressure composition isotherms, hydrogen storage capacity, hydrogen absorption kinetics and the desorption profile at different temperatures in detail. The Ti₂CrV crystallizes in body centered cubic (bcc) structure like TiCrV. The pressure composition isotherm of the alloy has been measured at room temperature and at 373K. The Ti₂CrV alloy shows maximum hydrogen storage capacity of 4.37 wt.% at room temperature. The cyclic hydrogen absorption capacity of Ti₂CrV alloy has been investigated at room temperature upto 10th cycle. The hydrogen storage capacity decreased progressively with cycling initially, but the alloy can maintain steady cyclic hydrogen absorption capacity 3.5 wt.% after 5th cycle. To get insight about the desorption behavior of the hydride in-situ desorption has been done at different temperatures and the amount of hydrogen desorbed has been calculated. The TG (Thermo gravimetric) and DTA analysis has been done on uncycled hydride shows that the surface poisoned sample gives a desorption onset temperature of 675K. The DSC measurement of uncycle and multi-cycled saturated hydrides shows that the hydrogen desorption temperature decreasing with cycling.