Ce_0.8Eu_0.2O_2-d Was synthesized by conventional solid state route as well as wet chemical route (i.e. cation complexation, combustion method). The crystallite size obtained for cation complexation and combustion samples is 14 and 19 nm while their surface area is 11.70 and 29.63 m² g^-1 respectively. Cation complexation synthesized product lead to formation of agglomerates and hence the sintered sample showed porosity compared to combustion synthesized sample. However, despite high packing density the combustion synthesized sample showed lower grain boundary, total conductivity than cation complexation synthesized product due to the formation of siliceous film at the grain boundary.