Non-Evaporable Getter (NEG) films of the Ti-Zr-V prepared on stainless steel substrates by Radio Frequency sputtering. To observe its getter behavior at the lowest activation temperature, the sample is heated continuously at different temperatures (100°C, 150°C, 200°C and 250°C) for 2 hours. The changes of the surface chemical composition at different temperatures are analyzed by using XPS and SEM (Scanning Electron Microscopy) techniques. The volume elemental composition of the film has been measured by energy dispersive X-ray spectroscopy (EDX). The in-situ XPS measurements of the activated getter films show the disappearance of the superficial oxide layer through the variation in the oxygen stoichiometry during thermal activation. Results of these studies show that the deposited films of Ti-Zr-V could be used as NEG to produce extreme high vacuum.