In this study, the impression creep behaviour of U–6 wt.%Zr alloy was studied in the temperature range 550–650 °C at different stresses. The velocity of the punch at different stresses and temperatures was evaluated for the above alloy. The creep curves at 575 °C showed a wavy phenomenon at all stresses. The stress exponents and thermal activation parameters of the above alloy were determined. A power law behaviour is displayed in the temperature range 600–650 °C with the stress exponents range from 8 to 8.4. The activation enthalpy for the U–6%Zr alloy was found to be independent of stress with an average value of 157 kJ/mol.