Uniform coating of β-silicon carbide (β-SiC) was formed over a graphite pellet through slurry-based silicon coating followed by in situ reaction at 1873 K (1600 °C). The coated pellet was exposed to molten lead-bismuth eutectic (LBE) at 1173 K (900 °C) in static condition for 200 h. Weight loss measurement, X-ray diffraction, and secondary electron microscopy–energy-dispersive spectroscopy confirmed that the SiC coating could effectively prevent molten LBE from attacking the inner graphite material.