The phase transitions in the LaCrO₃ were studied using bulk dilatometry and high temperature X-ray diffractometry from room temperature to 1050 and 1200°C, respectively. LaCrO₃ was prepared at 500°C from oxalate precursor employing microwave heating technique. Bulk shrinkage measurements on LaCrO₃ pellets were carried out using dilatometer designed and fabricated in our own laboratory. Dilatometric curves of LaCrO₃ showed two peaks in DL/L vs. temperature curves in the range 200–400 and 800–1000°C, respectively. These phase transitions have been confirmed using high temperature X-ray diffractometry. The role of simple technique like bulk dilatometry in detecting and monitoring the polymorphic transformations in solids is discussed for lanthanum chromates.