Evolution of transition metal charge states in correlation with the structural and magnetic properties in disordered double perovskites Ca2-xLaxFeRuO6 (0.5 <= x <= 2)

 
     
 
Author(s)

Naveen, K.; Rom, T.; Islam, S. S.; Yadav, A. K.; Jha, S. N.; Bhattacharyya, D.; and others
(A&MPD)

Source

Physical Chemistry Chemical Physics, 2021. Vol. 23: pp. 21769-21783

ABSTRACT

A series of disordered Ca1.5La0.5FeRuO6, CaLaFeRuO6 and La2FeRuO6 double perovskites were prepared by the solid-state reaction method and investigated by neutron powder diffraction, X-ray absorption near-edge structure (XANES) analysis at the Ru–K edge, Mössbauer spectroscopy, DC magnetization and resistivity measurements. All compounds crystallize in the orthorhombic crystal structure with the space group Pbnm down to 3 K, showing a random distribution of Fe and Ru at the B site. Thermogravimetric analysis indicates oxygen deficiency in the Ca-rich and formal oxygen hyperstoichiometry in the La-rich members of the present series. While Mössbauer spectra verify the Fe3+ state for all compositions, the XANES study reveals a variable Run+ oxidation state which decreases with increasing La content. The end member actually is a Ru3+/Ru4+ compound with possibly some cation vacancies. From magnetic susceptibility and neutron diffraction measurements, the presence of a G-type antiferromagnetic ordering was observed with a drastic increase in transition temperature from 275 K (Ca1.5La0.5FeRuO6) to 570 K (La2FeRuO6). Mössbauer spectroscopy confirms the presence of long-range ordering but, due to local variations in the exchange interactions, the magnetic states are microscopically inhomogeneous. All the samples are variable range hopping semiconductors. A complex interplay between structural features, charge states, anion or cation defects, and atomic disorder determines the magnetic properties of the present disordered 3d/4d double perovskite series.

 
 
SIRD Digital E-Sangrahay